Synthesis and Characterizations of TiO2/In2S3 Semiconductor Sensitized Solar Cell

Wagh VG, Bansode SB

The compact layer of Titania (TiO2) nanostructured films was made available for the fabrication of SSSC. TiO2 deposited by doctor blade method on FTO substrate which is acts as photoanode. The surface area of TiO2 was kept 0.25 cm2. In2S3 was deposited on FTO / TiO2 by chemical bath deposition method at room temperature in acidic as well as in alkaline bath. Without any further treatment prepared films were further used for the synthesis of photoelectrode of SSSCs. efficiency of fabricated solar cell in acidic as well as in alkaline bath is 0.034 and 0.007% respectively.